Preparation: Ensure proper isolation and disinfection of the treatment area.

Application: Dispense the required amount of putty onto a mixing pad.Using appropriate instruments, apply the putty directly into the prepared root canal or defect area.

Condensation: Condense the putty carefully to adapt it to the root canal walls or defect contours.

Cleaning: Remove any excess material and ensure proper adaptation within the canal or defect space.

Finalization: Verify proper placement and coverage, then proceed with further treatment steps as needed.

Evaluation: Confirm adequate setting and sealing of the putty through radiographic assessment or other diagnostic methods.

Post-treatment care: Follow up with appropriate post-treatment care instructions for the patient's recovery and maintenance.

SafeEndo BioStructure MTA Putty is a specialized dental material designed for root repair procedures. Developed using advanced material science, it contains Di- and Tri-Calcium Silicate along with Tricalcium Aluminate, ensuring superior clinical performance.

This bioactive and bioceramic root repair material offers excellent biocompatibility, high mechanical strength, and low solubility. It sets in the presence of moisture with a controlled setting time, allowing precise placement during dental procedures.

With high alkalinity and excellent radiopacity, it is ideal for a wide range of endodontic applications where effective sealing and long-term durability are essential. This innovative dental cement provides clinicians with a reliable solution for achieving predictable and lasting treatment outcomes

Key Features

• Bioactive & Bioceramic Composition
• Excellent Biocompatibility
• High Mechanical Strength
• Low Solubility
• Moisture-Activated Setting
• Controlled Setting Time
• High Alkalinity
• Radiopaque for Easy Detection
• Ready-to-Use Application

Working time at room temperature: 10+hrs

Initial Setting time at 37. C, invivo (or moist environment): Approx 4-5 hrs

Solubility: <4%

Dimensional Stability: +0.05-0.10% expansion

Color: Off White

Composition:

Mineral Trioxides: <80

Tricalcium Silicate

Dicalcium Silicate

Tricalcium Aluminate

Zirconium Oxide

Pate Forming Agents